The present paper focuses on the Spark Plasma Sintering (SPS) manufacturing of a new type of self-healing thermal barrier coating (TBC) and a study of its thermal cycling behaviour. The ceramic coating consists on an Yttria Partially Stabilized Zirconia (YPSZ) matrix into which healing agents made of MoSi2-Al2O3 core-shell particles are dispersed prior to sintering. The protocol used to sinter self-healing TBCs on MCrAlY (M: Ni or NiCo) pre-coated Ni-based superalloys is described and the reaction between the particles and the MCrAlY bond coating as well as the preventive solutions are determined. Thermal cycling experiments are performed on this complete multilayer system to study the crack healing behaviour. Post-mortem observations highlighted local healing of cracks due to the formation of silica and the subsequent conversion to zircon at the rims of the cracks.

Original languageEnglish
Pages (from-to)204-213
JournalMaterials & Design
Volume143
DOIs
Publication statusPublished - 2018

    Research areas

  • Ceramic matrix composites, High-temperature cyclic oxidation, Intermetallic particles, Multi-layer materials, Self-healing thermal barrier coatings, Spark plasma sintering

ID: 39387257