Significantly enhanced structural integrity of adhesively bonded PPS and PEEK composite joints by rapidly UV-irradiating the substrates

Dong Quan*, René Alderliesten, Clemens Dransfeld, Ioannis Tsakoniatis, Sofia Teixeira De Freitas, Gennaro Scarselli, Neal Murphy, Alojz Ivanković, Rinze Benedictus

*Corresponding author for this work

Research output: Contribution to journalArticleScientificpeer-review

17 Citations (Scopus)
58 Downloads (Pure)

Abstract

A high-power UV-irradiation technique was proposed for the surface treatment of PPS and PEEK composites, aiming to achieve good adhesion with epoxy adhesives. The composite substrates were rapidly UV-irradiated for a duration of between 2–30s, and then bonded using an aerospace film adhesive to produce joints. Tensile lap-shear strength and mode-I and mode-II fracture energies of the adhesive joints were investigated. It was observed that the application of a short-time UV-irradiation to the substrates transformed the failure mode of the specimens from adhesion failure to substrate damage in all cases. This consequently resulted in remarkable improvements in the mechanical and fracture performance of the adhesive joints. For example, the lap-shear strength increased from 11.8MPa to 31.7MPa upon UV-irradiating the PPS composites for 3s, and from 8.3MPa to 37.3MPa by applying a 5s UV-irradiation to the PEEK composites. Moreover, the mode-I and mode-II fracture energies significantly increased from ∼50J/m2 to ∼1500J/m2 and from <300J/m2 to ∼7000J/m2, respectively for both of the adhesively bonded PEEK and PPS composite joints.

Original languageEnglish
Article number108358
Number of pages11
JournalComposites Science and Technology
Volume199
DOIs
Publication statusPublished - 20 Oct 2020

Keywords

  • A: Adhesive joints
  • A: Polymer-matrix composites (PMCs)
  • B: Fracture toughness
  • B: Strength
  • E: Welding/joining

Fingerprint

Dive into the research topics of 'Significantly enhanced structural integrity of adhesively bonded PPS and PEEK composite joints by rapidly UV-irradiating the substrates'. Together they form a unique fingerprint.

Cite this